After two cycles of 40% cold tension and annealing, the grain size number changed from 1.5 to 8.5.
The strength, the linear strain hardening rate, and the hardness were enhanced significantly.
Cold expansion followed by annealing is a suitable method for manufacturing fine-grained heavy retaining rings.
Nucleation mechanisms of static recrystallization were given.