Modification of ceramic membranes with inorganic sorbents. Application to electrodialytic recovery of Cr(VI) anions from multicomponent solution

详细信息    查看全文

• 作者：Yu.S. Dzyazko^a ; ^{dzyazko@ionc.kiev.ua" class="auth_mail} ; ^{dzyazko@hotmail.com" class="auth_mail} ; A.S. Rudenko^a ; Yu.M. Yukhin^b ; A.V. Palchik^a ; V.N. Belyakov^a
• 关键词：Composite membranes ; Nanoparticles ; Electrodialysis ; Bismuth basic nitrate ; Hydrated zirconium dioxide ; Chromate
• 刊名：Desalination
• 出版年：2 June, 2014
• 年：2014
• 卷：342
• 期：Complete
• 页码：52-60
• 全文大小：1304 K

文摘

Composite membranes have been obtained by insertion of two-component modifier (up to 2.7 mass %) into pores of ceramics. The modifier included amorphous hydrated zirconium dioxide as well as crystalline bismuth basic nitrate Bi₆O₅(OH)₃(NO₃)₅鈭?#xA0;3H₂O, which is characterized by high sorption ability towards Cr(VI) anions due to formation of additional Cr-containing phases. The membranes were investigated with TEM, SEM and nitrogen adsorption technique. The modifier was found to exist in a form of aggregated nanoparticles, which evidently block macropores of ceramics and form secondary porous structure. The pores, which are attributed to the modifier, as well as its high surface charge density, provide selectivity of the composites towards anions in acidic media. Modification caused a decrease of their resistivity coefficient in 2.5-3.5 times in a comparison with pristine membrane, the composite materials do not obey Archie's law. The membranes were applied to electrodialytic recovery of Cr(VI) species from a highly concentrated solution, which contained also Cu(II), Ni(II) and Cr(III) cations. The most considerable current efficiency of Cr(VI) anions (46-92%) and the highest removal degree of these species (98%) were found for the composite material, which is characterized by the highest surface charge density (0.96C m^鈭?#xA0;2).