Effects preparation condition of multiwall carbon nanotube on Li intercalation were investigated in this study. Both Li intercalation and reversible capacities increased with increasing contact time of CH4 on Ni catalyst when the multiwall carbon nanotube was prepared. Raman spectroscopy suggested that the content of graphitic carbon tube increased with increasing the contact time of CH4 upon synthesis. Therefore, in case of tubular carbon, graphitic carbon also exhibited a larger capacity for Li intercalation comparing with that of amorphous one. Intercalation and reversible capacity for Li insertion at first cycle were attained to a value of 430 and 320mAh/g, respectively, on the carbon nanotube obtained at the contact time higher than 100g-cath/mol.