Permeability experiments were used to study hydrogen diffusion and trapping.
The trapping effect was less significant at a more negative charging potential.
The lattice diffusion coefficient of hydrogen was measured.
The densities of reversible hydrogen trap sites was ∼ 2 × 1018 sites cm−2.