Good dielectric temperature stability was found in BiAlO3-doped (Na, K, Li)NbO3.
Dielectric anomaly of ferroelectric–paraelectric transition was suppressed.
High-temperature dielectric relaxation was attributed to oxygen vacancies.
Ea is associated with both oxygen vacancy concentration and lattice parameters.