n and p doping effects on the optical gain of GaNAsBi-based QW was studied. Material gain was enhanced in p-i-n type quantum structure. After doping, a blue-shift of the fundamental transition was observed. Well width dependence of optical gain was examined. Bi composition was optimized in order to obtain QWs operating at 1.55 μm.