As a new structural and functional material, metal foam has been proven to obtain excellent properties when compared with dense ones. In the present paper, the powder metallurgy with a space holder technique was used to prepare magnesium foam. The porosity of the foam ranges from 38.90% to 57.50%, when the elastic modulus decreases from 8.50 GPa to 3.30 GPa, and the initial yield stress decreases from 24.90 MPa to 9.40 MPa. The magnesium foam has lower yield stress and longer stress platform, so it can be used as good cushioning energy absorbing materials.