Particle properties of submicron-sized WC-12Co processed by planetary ball milling
详细信息 查看全文
- 作者：Kristin M ; el ; Lutz Kr眉ger ; Christian Schimpf
- 关键词：Tungsten carbide cobalt ; Planetary ball milling ; Milling time ; Specific surface area ; Scanning electron microscopy ; X-ray diffraction
- 刊名：International Journal of Refractory Metals and Hard Materials
- 出版年：January, 2014
- 年：2014
- 卷：42
- 期：Complete
- 页码：200-204
- 全文大小：756 K
文摘
In this study, a conventional nano-grained tungsten carbide (WC) powder was mixed with 12 wt.% of a submicron cobalt (Co) powder in a ball mill for varying milling time periods, producing a homogeneous powder mixture which can be used to sinter near-nanocrystalline cemented carbides using short-duration sintering processes. Parameters of the wet milling process were adapted in order to maximise the mixing effect on the one hand, and to avoid particle growth during the milling process on the other. Surface analysis and microscopic examination of the milled powders showed a milling-time-dependent evolution of particle size and surface roughness. X-ray diffraction (XRD) investigation indicated a decrease of the crystallite size of WC in combination with an increase in defect density, as well as a strong increase in stacking faults in the Co. The main action of the milling mechanism is the fracturing of the WC particles. Co is distributed consistently around the WC particles. The preparation method used is a useful technique to prepare homogeneous powder mixtures of WC-Co with particle sizes below 200 nm on a laboratory scale.