Thermodynamic modeling of the Ge–Ti system supported by key experiment

详细信息    查看全文

• 作者：Dandan Liu^a ; ^b ; Huanli Yan^a ; Xiaoming Yuan^a ; Yoonsung Chung^c ; Yong Du^a ; ^{yongducalphad@gmail.com"" rel=""nofollow} ; Honghui Xu^a ; Libin Liu^b ; Philip Nash^c
• 关键词：Phase diagram ; Ge– ; Ti ; Calorimetry ; Thermodynamic modeling ; CALPHAD
• 刊名：Thermochimica Acta
• 出版年：2011
• 出版时间：10 July 2011
• 年：2011
• 卷：521
• 期：1-2
• 页码：148-154
• 全文大小：1118 K

文摘

A complete thermodynamic investigation of the Ge–Ti system was performed in this study. Seven samples were prepared by arc-melting the pure elements in order to check the literature data on phase diagram and enthalpy of formation of Ti₅Ge₃. The samples were annealed at certain temperatures for extended periods of time, and then quenched. Both the as-cast and annealed samples were examined by X-ray diffraction (XRD) analysis and scanning electron microscope (SEM) technology. The phase transformation temperatures were measured by differential thermal analysis (DTA). The measurement on enthalpy of formation for Ti₅Ge₃ was performed using the Kleppa-type HTRC with the calorimeter temperature set at 1100 ± 2 °C. Based upon the literature data and current experimental results, the Ge–Ti system was critically assessed by means of CALPHAD approach. The calculated phase diagram and thermodynamic properties agree well with the literature data and the present experimental results.