High Nb-containing TiAl alloy and Ti60 alloy was brazed using Ti-28Ni filler.
Increasing brazing temperature promoted the diffusion of Ni atoms into substrates.
Ti2Ni phase and Ti3Al phase were harmful to the joining properties.
The maximum shear strength of the joints was ∼140 MPa.