After ELM-like thermal shocks, tungsten was exposed to H/He particle fluxes.
The influence of combined loading conditions on the damage behaviour was studied.
Roughened surfaces do not alter H/He induced surface modifications.
Cracks interact with the particle flux, resulting in phenomena such as crack bridging.