Butt-coupling loss of 0.1dB/interface in InP/InGaAs MQW waveguide-waveguide structures grown by selective area chemical beam epitaxy
详细信息 查看全文
- 作者：Verschuren ; C.A. ; Harmsma ; P.J. ; Oei ; Y.S. ; Leys ; M.R. ; Vonk ; H. ; Wolter ; J.H.
- 关键词：42.82.&minus ; m ; 42.82.Ds ; 81.15.Hi ; Integrated optics ; Butt-coupling ; SAE ; CBE
- 刊名：Journal of Crystal Growth
- 出版年：1998
- 出版时间：June 1, 1998
- 年：1998
- 卷：188
- 期：1-4
- 页码：288-294
- 全文大小：1.27 M
文摘
The lateral coupling of waveguiding structures in both [0 1 1] and [0 1] directions is studied using embedded selective area epitaxy by chemical beam epitaxy. All growth steps are carried out under the same growth conditions on (1 0 0) InP substrates misoriented by 0.5° towards (1 1 1)B. Both planar and selectively grown material exhibits bright luminescence and narrow PL line widths (8 meV FWHM at 4 K), up to the lateral junction. Moreover, no degradation of the original material properties is observed after regrowth. SEM images show very flat layers and excellent lateral coupling for all four types of junctions. After reactive ion etching of waveguide ridges, the optical coupling losses have been determined using a Fabry–Perot setup at 1530 nm (TE polarization). Values of 0.1 to 0.2 dB/interface with excellent uniformity are presented for both perpendicular coupling directions. From our results we conclude that by optimization of the sample preparation prior to regrowth, values of 0.1 dB/interface can be obtained reproducibly.