Effect of hydrophobic paints coating for tritium reduction in concrete materials
详细信息 查看全文
- 作者：Y. Edao ; S. Fukada ; Y. Nishimura ; K. Katayama ; T. Takeishi ; Y. Hatano ; A. Taguchi
- 关键词：Tritium ; Concrete ; Hydrophobic paint ; Diffusion
- 刊名：Fusion Engineering and Design
- 出版年：2012
- 出版时间：August, 2012
- 年：2012
- 卷：87
- 期：7-8
- 页码：995-998
- 全文大小：753 K
文摘
The effects of hydrophobic paint coating on a concrete material of cement paste on the tritium transport are investigated. The cement paste is coated with two kinds of paints, acrylic-silicon resin paint and epoxy resin paint. We investigated the amount of tritium trapped in the samples exposed to tritiated water vapor by means of sorption and release. It was found that both the hydrophobic paints could reduce effectively tritium permeation during 50 days exposure of tritiated water vapor. The effect of tritium reduction of the epoxy paint was higher than that of silicon while the amount of tritium trapped in the epoxy paint was larger than that of silicon due to difference of the structure. Based on an analysis of a diffusion model, the rate-determining step of tritium migration through cement paste coated with the paints is diffusion through the paints respectively. It was found that tritium was easy to penetrate through silicon because there were many pores or voids in the silicon comparatively. In the case of tritium released from the epoxy paint, it is considered that tritium diffusion in epoxy is slow due to retardation by isotope exchange reaction to water included in epoxy paint.