Effect of Al substitution sites on Li1−pan style='font-style: italic'>xAlx(Ni0.5Co0.2Mn0.3)1−pan style='font-style: italic'>yAlyO2 cathode materials for lithium ion batteries
<p id="p0010">Li1−xAlx(Ni0.5Co0.2Mn0.3)1−yAlyO2 (NMCA) are synthesized by solid-state method.p>
•
<p id="p0015">LiAlO2 phase with high Lip>+p> ion diffusivity appears in Li1−xAlxNi0.5Co0.2Mn0.3O2.p>
•
<p id="p0020">Al prefers to form Alpxl.gif" class="glyphImg imgLazyJSB">pt>p://cdn.els-cdn.com/sd/entities/sbnd" class="glyphImg">pt>O solid solution in Li(Ni0.5Co0.2Mn0.3)1−yAlyO2 samples.p>
•
<p id="p0025">Alpxl.gif" class="glyphImg imgLazyJSB">pt>p://cdn.els-cdn.com/sd/entities/sbnd" class="glyphImg">pt>O solid solution improve the structural stability of LiNi0.5Co0.2Mn0.3O2.p>
•
<p id="p0030">Substitution of Li with low Al content has superior advantages for NMCA.p>