Hot deformation behavior and processing maps for coiled tubing steel

详细信息    查看全文

• 作者：Zhendong Zhang^a ; ^{zhendong.zhang@hotmail.com} ; Haitao Zhou^b ; ^{htzhou@csu.edu.cn} ; Xianghua Liu^a ; Sijun Li^c ; Jie Dong^c ; Guofei Si^b ; Bingyu Zhang^b ; Song Yue^b
• 关键词：Coiled tubing steel ; Processing map ; Hot deformation ; Dynamic recrystallization
• 刊名：Materials Science and Engineering: A
• 出版年：2013
• 出版时间：10 March, 2013
• 年：2013
• 卷：565
• 期：Complete
• 页码：213-218
• 全文大小：940 K

文摘

Hot compression test of coiled tubing steel is performed on Gleeble3500 at 850-1100 ¡ãC and strain rate from 0.001 s^?1 to 5 s^?1. It is found that the flow stress behavior is described by the hyperbolic sine constitutive equation in which the average activation energy of 390 kJ/mol is calculated. And the hot deformation behavior of coiled tubing steel is characterized by using processing maps developed on the basis of the dynamic materials model. The processing map shows the flow instable region and the flow stable region. The dynamic recovery (DRV) and dynamic recrystallization (DRX) occur in the stable region. In the processing map, the variation of the efficiency of the power dissipation is plotted as a function of temperature and strain rate. According to the processing map, the coiled tubing steel is rolled by the Thermo-Mechanical-Control-Process (TMCP), and finally it is obtained that the yield strength and tensile strength of coiled tubing steel are 565 MPa and 685 MPa respectively, and the elongation percentage is 32.1 % .