Lower rates of cross-linking reactions and higher conversion degrees were obtained in photo-DSC experiments with respect to real-time FT-IR spectroscopy. A limited amount (10 % wt) of HBP influenced to a certain extent the cure kinetics of the epoxy resin followed by RT-IR; a final conversion of epoxy groups equal to 100 % was achieved by increasing the content up to 20 % wt The addition of 10 % wt of HBP leaves the cure kinetics of the CE resin studied by p-DSC almost unchanged. By increasing the HBP content, a slightly lower reaction rate is observed at lower reaction times. The presence of the HBP produced a continuous decrease of the Tg of the UV-cured epoxy resin but only modest reductions in its thermo-oxidative stability.