Low irradiance photocatalytic degradation of toluene in air by screen-printed titanium dioxide layers
详细信息 查看全文
- 作者：Alberto Strini ; Aless ; ra Sanson ; Elisa Mercadelli ; Alex Sangiorgi ; Luca Schiavi
- 关键词：Photocatalysis ; Toluene ; Screen-printing ; Titanium dioxide ; Anatase&ndash ; rutile conversion
- 刊名：Thin Solid Films
- 出版年：2013
- 出版时间：31 October, 2013
- 年：2013
- 卷：545
- 期：Complete
- 页码：537-542
- 全文大小：2005 K
文摘
Screen-printed titania photocatalytic layers made from Degussa P25 were studied in order to assess the potential of this deposition technology for the production of catalytic surfaces for airborne pollutant degradation. The deposited catalytic TiO2 layers were characterized by a low density (about 25 % of the titania bulk crystal) typical of very porous films. The study was carried out using toluene at low concentration (12 ppb) as model pollutant and with a low UV-A irradiance level on the sample surface (200 ¦ÌW cm? 2). The catalyst layers were deposited on alumina and quartz substrates demonstrating a good catalytic depollution activity. The relationship between the layer thickness and the catalytic activity was studied in the 1 to 6.8 ¦Ìm range indicating an optimal 3-4 ¦Ìm film thickness. Thicker layers do not show significant increases in the catalytic activity. The optical transmittance was studied using quartz substrate samples, showing a severely reduced photon flux for layers deeper than 5 ¦Ìm. The effect of post-printing thermal treatment was studied in the 500-900 ¡ãC range, demonstrating good catalytic activity for processing temperatures ¡Ü 700 ¡ãC. These results indicate that the screen-printing process can be a promising technology for the realization of high efficiency photocatalytic materials for air depollution applications at low UV-A irradiance.