High temperature tribological behavior of nanostructured and conventional plasma sprayed alumina-titania coatings

详细信息    查看全文

• 作者：A. Rico ; ^{alvaro.rico@urjc.es} ; P. Poza ; J. Rodrí ; guez
• 关键词：Plasma sprayed coatings ; Alumina - titania ; Wear ; Mechanical properties
• 刊名：Vacuum
• 出版年：2013
• 出版时间：February, 2013
• 年：2013
• 卷：88
• 期：Complete
• 页码：149-154
• 全文大小：1123 K

文摘

Alumina-titania coatings are used where a high wear and oxidation resistances are required. These coatings are usually deposited by thermal spraying. The use of nanoparticles as feeding powders can lead to improved properties if some technological problems are solved. The small size of the nanoparticles makes necessary to prepare agglomerates able to be sprayed by conventional equipments. The plasma spray parameters should be chosen to maintain the starting nanostructure in the final coating. This can be achieved if the coating contains partially melted particles. In this work the mechanical and high temperature wear behaviour of Al₂O₃-13 % TiO₂ nanostructured coatings was compared to that of the conventional ones. Microstructural characterization was performed using scanning and transmission electron microscopy and X-rays diffraction techniques. Mechanical properties such as Young's modulus, hardness and fracture toughness were determined by depth sensing indentation. Wear rates and friction coefficients were measured by means of a Pin on disc machine in which both counterparts were made of Al₂O₃-13 % TiO₂. Experiments at different loads under unlubricated conditions, without elimination of the wear debris were carried out. Although the mechanical properties are slightly higher in the nanostructured coatings, they exhibit a much better wear behaviour under all the testing conditions.