Ultrasonic brazing of Al2O3/Cu was achieved in air without flux by Zn-14Al filler at 753 K. Newly formed crystalline Al2O3 aggregated at the ceramic interface. Overgrowth of intermetallic compounds generated by acoustic pits on Cu was found. Reaction wetting enhanced by ultrasonics dominated this rapid and high quality brazing.