A new warm press technique was employed to form dense slaked lime compacts.
A compact fabricated 150 °C and 240 MPa under uniaxial pressure for 90 min reached an average compressive strength of 57 MPa.
Warm press treatment led to mass transport occurred through a sintering-like process during warm pressing.