Pure delafossite AgFeO2 prepared by co-precipitation method.
57Fe Mössbauer spectroscopy studies performed at room and low temperatures.
Structural polytypes rhombohedral and hexagonal recognized by X-ray diffraction.
Transition from paramagnetic to magnetic ordering seen by Mössbauer spectroscopy.
Decrease of average hyperfine magnetic field observed with increase of temperature.