Coupling dissimilar oxides in heterostructures allows the engineering of interfacial, optical, charge separation/transport and transfer properties of photoanodes for photoelectrochemical (PEC) water splitting. Here, we demonstrate a double-heterojunction concept based on a BiVOb>4b>/WOb>3b>/SnOb>2b> triple-layer planar heterojunction (TPH) photoanode, which shows simultaneous improvements in the charge transport (∼93% at 1.23 V vs RHE) and transmittance at longer wavelengths (>500 nm). The TPH photoanode was prepared by a facile solution method: a porous SnOb>2b> film was first deposited on a fluorine-doped tin oxide (FTO)/glass substrate followed by WOb>3b> deposition, leading to the formation of a double layer of dense WOb>3b> and a WOb>3b>/SnOb>2b> mixture at the bottom. Subsequently, a BiVOb>4b> nanoparticle film was deposited by spin coating. Importantly, the WOb>3b>/(WOb>3b>+SnOb>2b>) composite bottom layer forms a disordered heterojunction, enabling intimate contact, lower interfacial resistance, and efficient charge transport/transfer. In addition, the top BiVOb>4b>/WOb>3b> heterojunction layer improves light absorption and charge separation. The resultant TPH photoanode shows greatly improved internal quantum efficiency (∼80%) and PEC water oxidation performance (∼3.1 mA/cm2 at 1.23 V vs RHE) compared to the previously reported BiVOb>4b>/WOb>3b> photoanodes. The PEC performance was further improved by a reactive-ion etching treatment and CoOb>xb> electrocatalyst deposition. Finally, we demonstrated a bias-free and stable solar water-splitting by constructing a tandem PEC device with a perovskite solar cell (STH ∼3.5%).