Assembling Conductive PEBA Copolymer at the Continuous Interface in Ternary Polymer Systems: Morphology and Resistivity

详细信息    查看全文

• 作者：Jun Wang ; Alejandra Reyna-Valencia ; Basil D. Favis
• 刊名：Macromolecules
• 出版年：2016
• 出版时间：July 26, 2016
• 年：2016
• 卷：49
• 期：14
• 页码：5115-5125
• 全文大小：553K
• 年卷期：0
• ISSN：1520-5835

文摘

Two ternary blend systems of low-density polyethylene/poly(ether-block-amide)/polyethylene terephthalate (LDPE/PEBA/PET) and LDPE/PEBA/polyvinylidene fluoride (PVDF) are prepared by melt blending to thermodynamically assemble the ionically conductive PEBA copolymer at the continuous interface. The LDPE/PEBA/PET blend demonstrates weak partial wetting and a novel morphology transition to complete wetting was observed as the PEBA composition increases from 3% to about 10%. The phenomena can be explained by a mechanism based on the competition between dewetting and coalescence of the PEBA phase at the interface. In the completely wet LDPE/PEBA/PVDF system, a minimum concentration is required to form intact PEBA layers with a thickness of ∼100 nm. Assembling PEBA at the interface of the ternary systems results in the formation of conductive pathways of very low percolation thresholds and thus leads to a significant reduction in the resistivity for both ternary systems as compared to binary blends with PEBA. A particularly sharp drop in resistivity is observed for the complete wetting morphology of LDPE/PEBA/PVDF.