f new solid acid proton conductors, we prepared the solid acid rubidium methane phosphonate(RMP). These crystals have a monoclinic structure (
P2/
c;
a = 9.3452,
b = 9.3142, and
c = 7.5021 Å;
![](/images/gi<font color=)
fchars/beta2.gi
f" BORDER=0 ALIGN="middle"> =101.12). The salt incorporates a hydrated lamellar structure. The
1H MAS NMR reveals two di
fferent typeso
f acidic protons as well as the water protons in the lamella. The
1H VT MAS NMR o
f RMP·2H
2O singlecrystal shows a structural phase transition around 320 K, and the high-temperature phase exhibits signi
ficantproton dynamics. The proton proximities are established by solid state
1H DQF NMR. The dehydration o
fRMP crystal leads to structural collapse, and the resultant RMP powder is extremely hygroscopic. The protonenvironment and dynamics are examined using
1H DQF NMR, which reveals that the dehydrated RMP powderhas rigid lattice, in contrast with the hydrated
form. Further the
1H VT MAS NMR shows that dehydratedRMP powder has no phase transition, and no signi
ficant proton dynamics are observed in the temperaturerange o
f 250-350 K. The new hydrated crystal, RMP·2H
2O, shows high proton mobility at relatively lowtemperature (~330 K) and a proton transport mechanism that uniquely relies on crystalline water.