Synthesis and Characterization of Well-Controlled Isotactic Polypropylene Ionomers Containing Ammonium Ion Groups
详细信息 查看全文
- 作者：Min Zhang ; Xuepei Yuan ; Lu Wang ; T. C. Mike Chung ; Tianzi Huang ; Willem deGroot
- 刊名：Macromolecules
- 出版年：2014
- 出版时间：January 28, 2014
- 年：2014
- 卷：47
- 期：2
- 页码：571-581
- 全文大小：445K
- ISSN：1520-5835
文摘
This paper discusses the synthesis of a new family of well-controlled isotactic polypropylene ionomers (iPP-NH3+Cl鈥?/sup>) containing up to 5 mol % of NH3+Cl鈥?/sup> ionic groups, with high molecular weight and narrow molecular weight and composition distributions, as well as good processability in melt and solution. A systematic study was conducted using various isospecific Ziegler鈥揘atta and metallocene catalysts in the copolymerization of propylene and a high 伪-olefin comonomer containing a silane-protected amino group and the subsequent work-up procedures that can prevent undesirable side reactions in forming iPP-NH3+Cl鈥?/sup> ionomers in a one-pot process. The resulting copolymers were carefully monitored by polymer solubility and a combination of NMR, GPC-triple detectors, DSC, and mechanical property measurements. Evidently, the most suitable reaction process requires a combination of the rac-Me2Si[2-Me-4-Ph(Ind)]2ZrCl2 metallocene catalyst system with a purified d-MAO (TMA-free), 6-bis(trimethylsilyl)amino-1-hexene comonomer during the copolymerization reaction and a work-up procedure to directly interconvert the silane-protected amino groups (鈭扤(SiMe3)2) into 鈭扤H3+Cl鈥?/sup> ionic groups before exposing to air. The attempt of isolating both iPP-N(SiMe3)2 and iPP-NH2 intermediates resulted in the insoluble (cross-linked) products. On the other hand, the resulting iPP-NH3+Cl鈥?/sup> ionomers were melt processed in air and showed a systematic increase of mechanical properties and high-temperature stability with the increase of NH3+Cl鈥?/sup> content.