文摘
A new thermodynamically stable, aperiodic 鈥渂ricks-and-mortar鈥?(B&M) cellular mesophase structure is reported in PS1-b-(PI-b-PS2)3 miktoarm copolymer and PS homopolymer blends [PS1, long polystyrene; PI, poly(isoprene); PS2, short polystyrene], where PS comprises discrete hard 鈥渂ricks鈥?and PI the continuous soft 鈥渕ortar鈥? The mesophase is unique in its extreme domain volume fractions, its lack of positional order, and quasi-long-range orientational order. On the basis of this unusual mesophase structure, a series of PS-based thermoplastic elastomers are realized, combining rigidity from an exceptionally high content of discrete glassy PS domains (up to 82 wt %) and high extensibility with recoverable elasticity from a low content of continuous rubbery PI (down to 18 wt %). The new elastomers show sharp yielding behavior while maintaining good elasticity at large strains. Tensile-SAXS experiments reveal that voiding plays an important role for the mechanical behavior and voids can open/close reversibly with/without loading. Plastic deformation only results in a slight loss of recoverable elasticity.