Environment Controlled Dewetting of Rh鈥揚d Bilayers: A Route for Core鈥揝hell Nanostructure Synthesis

详细信息    查看全文

• 作者：Gintautas Abrasonis ; Sebastian Wintz ; Maciej O. Liedke ; Funda Aksoy Akgul ; Matthias Krause ; Karsten Kuepper ; Dipanjan Banerjee ; Zhi Liu ; Sibylle Gemming
• 刊名：The Journal of Physical Chemistry C
• 出版年：2012
• 出版时间：July 12, 2012
• 年：2012
• 卷：116
• 期：27
• 页码：14401-14407
• 全文大小：411K
• 年卷期：v.116,no.27(July 12, 2012)
• ISSN：1932-7455

文摘

Chemical environment plays a significant role on the size, shape, or surface composition of nanostructures. Here, the chemical environment effects are studied in the context of core鈥搒hell nanoparticle synthesis. The environment driven dynamics and kinetics of Rh/Pd bilayers is investigated by in situ ambient pressure X-ray photoelectron spectroscopy. Thin Rh (1.5 nm)/Pd ( 1.5 nm) bilayers were grown on thermally oxidized Si substrates. The films were heated in CO or NO environments or heated in vacuum with a subsequent NO/CO cycling. This study demonstrates that not the initial stacking sequence but the chemical environment plays a crucial role in controlling the surface composition. Heating in CO results in a surface enrichment of Pd at 200 掳C and is followed by film dewetting at 300 掳C. Heating in NO results in progressive oxidation of Rh starting at 150 掳C, which stabilizes the film continuity up to >375 掳C. The film rupture correlates with the thermal destabilization of the surface oxide. Heating in vacuum results in a significant increase in surface Pd concentration, and the following NO/CO cycling induces periodic surface composition changes. The quasi-equilibrium states are 50% and 20% of Rh/(Rh + Pd) for NO and CO environments, respectively. Possible surface composition change and dewetting mechanisms are discussed on the basis of the interplay of thermodynamic (surface/oxide energy and surface wetting) and kinetic (surface oxidation and thermally induced and chemically enhanced diffusion) factors. The results open alternative ways to synthesize supported (core鈥搒hell) nanostructures with controlled morphology and surface composition.