Enhanced Surface Plasmon Effect of Ag/TiO2 Nanodiodes on Internal Photoemission
详细信息 查看全文
- 作者：Hyosun Lee ; Young Keun Lee ; Euyheon Hwang ; Jeong Young Park
- 刊名：Journal of Physical Chemistry C
- 出版年：2014
- 出版时间：March 20, 2014
- 年：2014
- 卷：118
- 期：11
- 页码：5650-5656
- 全文大小：332K
- 年卷期：v.118,no.11(March 20, 2014)
- ISSN：1932-7455
文摘
Over the last several decades, innovative light-harvesting devices have evolved to achieve high-efficiency solar energy transfer. Understanding the mechanism of plasmon resonance is very desirable to overcome the conventional efficiency limits of photovoltaics. The influence of localized surface plasmon resonance on hot electron flow at a metal鈥搒emiconductor interface was observed with a Schottky diode composed of a thin silver layer on TiO2; subsequent X-ray photoelectron spectroscopy characterized how oxygen in the Ag/TiO2 nanodiode influenced the Schottky barrier height. Photoexcited electrons generate photocurrent when they have enough energy to travel over the Schottky barrier formed at the metal鈥搒emiconductor interface. We observed that the photocurrent could be enhanced by optically excited surface plasmons. When the surface plasmons are excited on the corrugated Ag metal surface, they decay into energetic hot electron鈥揾ole pairs, contributing to the total photocurrent. The abnormal resonance peaks observed in the incident photons to current conversion efficiency can be attributed to surface plasmon effects. We observed that photocurrent enhancement due to surface plasmons was closely related to the corrugation (or roughness) of the metal surface. While the photocurrent measured on Ag/TiO2 exhibits surface plasmon peaks, the photocurrent on Au/TiO2 does not show any peaks even at the Au surface plasmon energy frequency presumably because of the smoothness of the gold film. We modified the thickness and morphology of a continuous Ag layer using electron beam evaporation deposition and heating under gas conditions and found that morphological changes and the thickness of the Ag film are key factors in controlling the internal photoemission efficiency.