文摘
The ability to create a synergistic effect of nanostructure engineering and its hybridization with conductive carbonaceous material is highly desirable for attaining high-performance lithium ion batteries (LIBs). Herein, we judiciously crafted ZnFe2O4/carbon nanocomposites composed of ZnFe2O4 nanoparticles with an average size of 16 ± 5 nm encapsulated within the continuous carbon network as anode materials for LIBs. Such intriguing nanocomposites were yielded in situ via the pyrolysis-induced carbonization of polystyrene@poly(acrylic acid) (PS@PAA) core@shell nanospheres in conjunction with the formation of ZnFe2O4 nanoparticles through the thermal decomposition of ZnFe2O4 precursors incorporated within the PS@PAA nanospheres. By systematically varying the ZnFe2O4 content in the ZnFe2O4/carbon nanocomposites, the nanocomposite containing 79.3 wt % ZnFe2O4 was found to exhibit an excellent rate performance with high capacities of 1238, 1198, 1136, 1052, 926, and 521 mAh g–1 at specific currents of 100, 200, 500, 1000, 2000, and 5000 mA g–1, respectively. Moreover, cycling performance of the ZnFe2O4/carbon nanocomposite with 79.3 wt % ZnFe2O4 at specific currents of 200 mA g–1 delivered an outstanding prolonged cycling stability for several hundred cycles.