Fabrication of Binder-Free Pencil-Trace Electrode for Lithium-Ion Battery: Simplicity and High Performance
详细信息    查看全文
文摘
A binder-free and solvent-free pencil-trace electrode with intercalated clay particles (mainly SiO2) is prepared via a simple pencil-drawing process on grinded Cu substrate with rough surface and evaluated as an anode material for lithium-ion battery. The pencil-trace electrode exhibits a high reversible capacity of 672 mA h g–1 at 100 mA g–1 after 100 cycles, which can be attributed to the unique multilayered graphene particles with lateral size of few micrometers and the formation of LixSi alloys generated by interaction between Li+ and an active Si produced in the electrochemical reduction of nano-SiO2 in the clay particles between the multilayered graphene particles. The multilayered graphene obtained by this process consists of 1 up to 20 and occasionally up to 50 sheets and thus can not only help accommodating the volume change and alleviating the structural strain during Li ion insertion and extraction but also allow rapid access of Li ions during charge–discharge cycling. Drawing with a pencil on grinded Cu substrate is not only very simple but also cost-effective and highly scalable, easily establishing graphitic circuitry through a solvent-free and binder-free approach.

© 2004-2018 中国地质图书馆版权所有 京ICP备05064691号 京公网安备11010802017129号

地址:北京市海淀区学院路29号 邮编:100083

电话:办公室:(+86 10)66554848;文献借阅、咨询服务、科技查新:66554700