• 作者：Shou-Hang Bo ; Clare P. Grey ; Peter G. Khalifah
• 刊名：Chemistry of Materials
• 出版年：2015
• 出版时间：July 14, 2015
• 年：2015
• 卷：27
• 期：13
• 页码：4630-4639
• 全文大小：458K
• ISSN：1520-5002

文摘

The reversible room temperature intercalation of Mg²⁺ ions is difficult to achieve but may offer substantial advantages in the design of next-generation batteries if this electrochemical process can be successfully realized. Two types of quadruple ribbon-type transition metal borates (Mg_xFe_2鈥?i>xB₂O₅ and MgVBO₄) with high theoretical capacities (186 and 360 mAh/g) have been synthesized and structurally characterized through the combined Rietveld refinement of synchrotron and time-of-flight neutron diffraction data. Neither MgVBO₄ nor Mg_xFe_2鈥?i>xB₂O₅ can be chemically oxidized at room temperature, though Mg can be dynamically removed from the latter phase at elevated temperatures (approximately 200鈥?00 掳C). It is found that Mg diffusion in the Mg_xFe_2鈥?i>xB₂O₅ structure is more facile for the inner two octahedral sites than for the two outer octahedral sites in the ribbons, a result supported by both the refined site occupancies after Mg removal and bond valence sum difference map calculations of diffusion paths in the pristine material. Mg diffusion in this pyroborate Mg_xFe_2鈥?i>xB₂O₅ framework is also found to be tolerant to the presence of Mg/Fe disorder since Mg ions can diffuse through interstitial channels which bypass Fe-containing sites.