Silica-Coated and Bare Akaganeite Nanorods: Structural and Magnetic Properties

详细信息    查看全文

• 作者：Marin Tadic ; Irena Milosevic ; Slavko Kralj ; Mamadou Mbodji ; Laurence Motte
• 刊名：Journal of Physical Chemistry C
• 出版年：2015
• 出版时间：June 18, 2015
• 年：2015
• 卷：119
• 期：24
• 页码：13868-13875
• 全文大小：498K
• ISSN：1932-7455

文摘

We report on structural and magnetic properties of uniform silica-coated akaganeite nanorods with length of L 鈭?80 卤 15 nm and diameter D 鈭?15 卤 5 nm as well as silica shell thickness of about 5 nm. Unexpected negative difference between field-cooled (FC) and zero-field-cooled (ZFC) magnetization 螖M = M_FC 鈥?M_ZFC < 0, room temperature ferromagnetism, and exchange bias effect have been found. The nanorods are investigated by X-ray powder diffraction (XRPD), transmission electron microscopy (TEM), and vibrating sample magnetometer (VSM) measurements. The magnetic measurements were also performed on bare akaganeite nanorods in order to discriminate the effects of silica coating on the magnetic properties. The measured coercivity and exchange bias effect of bare 尾-FeOOH nanorods are much lower compared with same properties of SiO₂@尾-FeOOH nanorods, emphasizing the effect of silica coating on the magnetic properties. These results are discussed considering the core鈥搒hell structure of akaganeite nanorods; i.e., the inner part of the akaganeite nanorod has antiferromagnetic ordering, whereas the nanorod surface exhibits some disorder spin state.