Electropolymerizable 2,2′-Carboranyldithiophenes. Structure−Property Investigations of the Corresponding Conducting Polymer Films by Electrochemistry, UV−Visible Spectroscopy and Con

详细信息    查看全文

• 作者：Frdric Barrire ; Bruno Fabre ; Erhong Hao ; Zorabel M. LeJeune ; Euiyong Hwang ; Jayne C. Garno ; Evgueni E. Nesterov ; M. Graa H. Vicente
• 刊名：Macromolecules
• 出版年：2009
• 出版时间：April 28, 2009
• 年：2009
• 卷：42
• 期：8
• 页码：2981-2987
• 全文大小：297K
• 年卷期：v.42,no.8(April 28, 2009)
• ISSN：1520-5835

文摘

Carborane-functionalized conducting polymer films have been electrogenerated in dichloromethane from the anodic oxidation of ortho- (1), meta- (3) and para-carborane (4) isomers linked to two 2-thienyl units. The corresponding electrochemical response was characterized by a broad reversible redox system corresponding to the p-doping/undoping of the polythiophene backbone, the formal potential of which increased in the order poly(1) < poly(3) < poly(4), from ca. 0.50 to 1.15 V vs Ag/Ag⁺ 10⁻² M. From further UV−visible spectroscopy analysis, the optical band gap was estimated at 1.8, 2.0 and 2.2 eV for poly(1), poly(3) and poly(4), respectively. The more conjugated and electroconductive character of poly(1) is ascribed to a more planar conformation of the conjugated backbone resulting from an intramolecular β−β′ cyclization reaction in the monomer, consequently yielding a fused conjugated polymer. Molecular modeling calculations using the DFT method support this hypothesis. The surface topography and maps of the conductive domains of the electropolymerized films were evaluated by conducting probe AFM. The three polymers exhibit fairly similar morphological characteristics and a surface roughness of 2 nm. Current−voltage (I−V) characteristics of conducting AFM tip-carborane polymer−ITO junctions showed that poly(1) had the highest conductivity.