White Light-Activated Antimicrobial Paint using Crystal Violet
详细信息 查看全文
- 作者：Gi Byoung Hwang ; Elaine Allan ; Ivan P. Parkin
- 刊名：ACS Applied Materials & Interfaces
- 出版年：2016
- 出版时间：June 22, 2016
- 年：2016
- 卷：8
- 期：24
- 页码：15033-15039
- 全文大小：399K
- 年卷期：0
- ISSN：1944-8252
文摘
Crystal violet (CV) was incorporated into acrylic latex to produce white-light-activated antimicrobial paint (WLAAP). Measurement of the water contact angle of the WLAAP showed that the water contact angle increased with increasing CV concentration. In a leaching test over 120 h, the amount of CV that leached from the WLAAPs was close to the detection limit (<0.03%). The WLAAPs were used to coat samples of polyurethane, and these showed bactericidal activity against Escherichia coli, which is a key causative agent of healthcare-associated infections (HAIs). A reduction in the numbers of viable bacteria was observed on the painted coated polyurethane after 6 h in the dark, and the bactericidal activity increased with increasing CV concentration (P < 0.1). After 6 h of white light exposure, all of coated polyurethanes demonstrated a potent photobactericidal activity, and it was statistically confirmed that the WLAAP showed better activity in white light than in the dark (P < 0.05). At the highest CV concentration, the numbers of viable bacteria fell below the detection limit (<103 CFU/mL) after 6 h of white light exposure. The difference in antimicrobial activity between the materials in the light and dark was 0.48 log at CV 250 ppm, and it increased by 0.43 log at each increment of CV 250 ppm. The difference was the highest (>1.8 log) at the highest CV concentration (1000 ppm). These WLAAPs are promising candidates for use in healthcare facilities to reduce HAIs.