Superparamagnetic Nanocomposites Based on the Dispersion of Oleic Acid-Stabilized Magnetite Nanoparticles in a Diglycidylether of Bisphenol A-Based Epoxy Matrix: Magnetic Hyperthermia and Shape Memory

详细信息    查看全文

• 作者：J. Puig ; C. E. Hoppe ; L. A. Fasce ; C. J. P茅rez ; Y. Pi帽eiro-Redondo ; M. Ba帽obre-L贸pez ; M. A. L贸pez-Quintela ; J. Rivas ; R. J. J. Williams
• 刊名：The Journal of Physical Chemistry C
• 出版年：2012
• 出版时间：June 21, 2012
• 年：2012
• 卷：116
• 期：24
• 页码：13421-13428
• 全文大小：444K
• 年卷期：v.116,no.24(June 21, 2012)
• ISSN：1932-7455

文摘

Superparamagnetic nanocomposites were obtained by dispersion of oleic acid (OA)-coated magnetite NPs in an epoxy system based on diglycidylether of bisphenol A (DGEBA) modified with OA. Dispersion of conventional oleic acid-stabilized magnetite NPs in a typical epoxy matrix is not possible due to the dissimilar chemical structures of the organic coating and the reactive solvent. However, by modification of a DGEBA-based epoxy with 20 wt % OA, we obtained a suitable reactive solvent to disperse up to at least 8 wt % of OA-stabilized magnetite NPs. A tertiary amine was used to catalyze the epoxy鈥揳cid reaction and initiate the homopolymerization of the epoxy excess. Both reactions occurred practically in series, first the epoxy鈥揳cid and then the epoxy homopolymerization. It was necessary to complete the first reaction to attain a very good dispersion of magnetite NPs in the reactive solvent previous to the occurrence of the final reaction. Magnetization curves and TEM images revealed a uniform dispersion of individual nanoparticles in the cross-linked epoxy. A sample containing 8 wt % OA-coated magnetite NPs exhibited a temperature increase of 25 掳C at its surface when exposed to an alternating magnetic field. The temperature increase was enough to induce the shape memory effect of the nanocomposite.