High-Temperature CaO Hydration/Ca(OH)2 Decomposition over a Multitude of Cycles
详细信息 查看全文
- 作者：Shiying Lin ; Yin Wang ; Yoshiizo Suzuki
- 刊名：Energy & Fuels
- 出版年：2009
- 出版时间：June 18, 2009
- 年：2009
- 卷：23
- 期：6
- 页码：2855-2861
- 全文大小：518K
- 年卷期：v.23,no.6(June 18, 2009)
- ISSN：1520-5029
文摘
CaO hydration and Ca(OH)2 decomposition cycles can be used to supply or transport energy (heat). The reaction rates and properties of these materials are important parameters for the design of a reactor. In this work, the rates of CaO hydration and Ca(OH)2 decomposition were measured continuously over 20 hydration/decomposition cycles by means of a high-pressure thermogravimetric apparatus. CaO was completely converted to Ca(OH)2 in all cycles, but the CaO hydration rate decreased with increasing number of cycles. Ca(OH)2 was decomposed to CaO completely in all cycles. The extent and rate of conversion for Ca(OH)2 decomposition were not influenced by increasing cycle number. Eutectic melting of CaO and Ca(OH)2 was not observed on the particles after CaO hydration or after Ca(OH)2 decomposition. The compressive strength of CaO particles decreased with increasing cycle number, and the average compressive strength of CaO particles after 20 cycles was about 16.5 kg/cm2.