Amorphous vanadium oxide/carbon composite (V2O5/C) was first applied to the positive electrode active material for rechargeable aluminum batteries. Electrochemical properties of V2O5/C were investigated by cyclic voltammetry and charge鈥揹ischarge tests. Reversible reduction/oxidation peaks were observed for the V2O5/C electrode and the rechargeable aluminum cell showed the maximum discharge capacity over 200 mAh g鈥? in the first discharging. The XPS analyses after discharging and the following charging exhibited that the redox of vanadium ion in the V2O5/C active material occurred during discharging and charging, and the average valence of V changed between 4.14 and 4.85.