Structure and Biodegradation Mechanism of Milled Bombyx mori Silk Particles

详细信息    查看全文

• 作者：Rangam Rajkhowa ; Xiao Hu ; Takuya Tsuzuki ; David L. Kaplan ; Xungai Wang
• 刊名：Biomacromolecules
• 出版年：2012
• 出版时间：August 13, 2012
• 年：2012
• 卷：13
• 期：8
• 页码：2503-2512
• 全文大小：567K
• 年卷期：v.13,no.8(August 13, 2012)
• ISSN：1526-4602

文摘

The aim of this study was to understand the structure and biodegradation relationships of silk particles intended for targeted biomedical applications. Such a study is also useful in understanding structural remodelling of silk debris that may be generated from silk-based implants. Ultrafine silk particles were prepared using a combination of efficient wet-milling and spray-drying processes with no addition of chemicals other than those used in degumming. Milling reduced the intermolecular stacking forces within the 尾-sheet crystallites without changing the intramolecular binding energy. Because of the rough morphology and the ultrafine size of the particles, degradation of silk particles by protease XIV was increased by about 3-fold compared to silk fibers. Upon biodegradation, the thermal degradation temperature of silk increased, which was attributed to the formation of tight aggregates by the hydrolyzed residual macromolecules. A model of the biodegradation mechanism of silk particles was developed based on the experimental data. The model explains the process of disintegration of 尾-sheets, supported by quantitative secondary structural analysis and microscopic images.