Atomic Layer Epitaxy of h-BN(0001) Multilayers on Co(0001) and Molecular Beam Epitaxy Growth of Graphene on h-BN(0001)/Co(0001)

详细信息    查看全文

• 作者：M. Sky Driver ; John D. Beatty ; Opeyemi Olanipekun ; Kimberly Reid ; Ashutosh Rath ; Paul M. Voyles ; Jeffry A. Kelber
• 刊名：Langmuir
• 出版年：2016
• 出版时间：March 22, 2016
• 年：2016
• 卷：32
• 期：11
• 页码：2601-2607
• 全文大小：390K
• ISSN：1520-5827

文摘

The direct growth of hexagonal boron nitride (h-BN) by industrially scalable methods is of broad interest for spintronic and nanoelectronic device applications. Such applications often require atomically precise control of film thickness and azimuthal registry between layers and substrate. We report the formation, by atomic layer epitaxy (ALE), of multilayer h-BN(0001) films (up to 7 monolayers) on Co(0001). The ALE process employs BCl₃/NH₃ cycles at 600 K substrate temperature. X-ray photoelectron spectroscopy (XPS) and low energy electron diffraction (LEED) data show that this process yields an increase in h-BN average film thickness linearly proportional to the number of BCl₃/NH₃ cycles, with BN layers in azimuthal registry with each other and with the Co(0001) substrate. LEED diffraction spot profile data indicate an average BN domain size of at least 1900 Å. Optical microscopy data indicate the presence of some domains as large as ∼20 μm. Transmission electron microscopy (TEM) and ambient exposure studies demonstrate macroscopic and microscopic continuity of the h-BN film, with the h-BN film highly conformal to the Co substrate. Photoemission data show that the h-BN(0001) film is p-type, with band bending near the Co/h-BN interface. Growth of graphene by molecular beam epitaxy (MBE) is observed on the surface of multilayer h-BN(0001) at temperatures of 800 K. LEED data indicate azimuthal graphene alignment with the h-BN and Co(0001) lattices, with domain size similar to BN. The evidence of multilayer BN and graphene azimuthal alignment with the lattice of the Co(0001) substrate demonstrates that this procedure is suitable for scalable production of heterojunctions for spintronic applications.