文摘
To produce biocompatible, mechanically robust, and conductive materials for bone tissue engineering, chemical oxidation using sodium hyprochlorite (NaClO) was utilized to introduce carboxyl groups onto silk fibroin (SF). A final carboxyl content of 1.09 mM/g SF was obtained, corresponding to ∼47% of the primary hydroxymethyl groups on the silk. Interestingly, both infrared (IR) spectroscopy and circular dichroism (CD) spectra demonstrated that the resulting oxidized silk (OxSF) self-assembled into β-sheet structures under aqueous conditions and this contributed to the mechanical properties of the as-prepared silk-based scaffolds and the mineralized OxSF scaffolds (M-OxSF). The OxSF scaffolds had a compressive modulus of 211 ± 75 KPa in the hydrated state, 10 times higher than that of the SF scaffolds, and the modulus of the M-OxSF scaffolds was increased to 758 ± 189 KPa. Human bone marrow-derived mesenchymal stem cells (hMSCs) grown on the scaffolds during osteogenesis showed that the OxSF scaffolds supported the proliferation and differentiation of hMSCs in vitro.