Wettability of Nafion and Nafion/Vulcan Carbon Composite Films

详细信息    查看全文

• 作者：Xiaoan Li ; Fangxia Feng ; Ke Zhang ; Siyu Ye ; Daniel Y. Kwok ; Viola Birss
• 刊名：Langmuir
• 出版年：2012
• 出版时间：April 24, 2012
• 年：2012
• 卷：28
• 期：16
• 页码：6698-6705
• 全文大小：450K
• 年卷期：v.28,no.16(April 24, 2012)
• ISSN：1520-5827

文摘

The wettability of the Pt/carbon/Nafion catalyst layer in proton exchange membrane fuel cells is critical to their performance and durability, especially the cathode, as water is needed for the transport of protons to the active sites and is also involved in deleterious Pt nanoparticle dissolution and carbon corrosion. Therefore, the focus of this work has been on the first-time use of the water droplet impacting method to determine the wettability of 100% Nafion films, as a benchmark, and then of Vulcan carbon (VC)/Nafion composite films, both deposited by spin-coating in the Pt-free state. Pure Nafion films, shown by SEM analysis to have a nanochanneled structure, are initially hydrophobic but become hydrophilic as the water droplet spreads, likely due to reorientation of the sulfonic acid groups toward water. The wettability of VC/Nafion composite films depends significantly on the VC/Nafion mass ratios, even though Nafion is believed to be preferentially oriented (sulfonate groups toward VC) in all cases. At low VC contents, a significant water droplet contact angle hysteresis is seen, similar to pure Nafion films, while at higher VC contents (>30%), the films become hydrophobic, also exhibiting superhydrophobicity, with surface roughness playing a significant role. At >80% VC, the surfaces become wettable again as there is insufficient Nafion loading present to fully cover the carbon surface, allowing the calculation of the Nafion:carbon ratio required for a full coverage of carbon by Nafion.