In situ synthesis of TiO2-functionalized metal nanoparticles

详细信息    查看全文

• 作者：David M. King ; Yun Zhou ; Luis F. Hakim ; Xinhua Liang ; Peng Li ; Alan W. Weimer
• 刊名：Industrial & Engineering Chemistry Research
• 出版年：2009
• 出版时间：January 7, 2009
• 年：2009
• 卷：48
• 期：1
• 页码：352-360
• 全文大小：488K
• 年卷期：v.48,no.1(January 7, 2009)
• ISSN：1520-5045

文摘

The ability to prepare and functionalize passivated nanosized metal powders was demonstrated using TiO₂ films that were deposited via atomic layer deposition (ALD). Metal nanopowders were synthesized from the dehydration and subsequent decomposition of bulk quantities of metal oxalates in a fluidized-bed reactor. The gas-phase TiO₂ ALD coating process was used to passivate these particles in situ, which alleviated the need to expose the oxygen-sensitive materials to air. Metal oxalate size reduction was achieved using a cryogenic milling process that reduced the micrometer-sized oxalate feed powder and yielded metal nanopowders with an average primary diameter of 50 nm. The metal oxalates that have received the most attention are those of iron, nickel, cobalt, and copper. Al₂O₃-based ALD films have been deposited on each of these metals, whereas TiO₂:metal nanocomposite powder research has been performed here and is the basis for this work.