Yolk–shell TiO<sub>2sub>@C nanocomposites have been synthesized successfully through a simple self-catalyzing solvothermal method. The structural and morphological characterizations reveal that TiO<sub>2sub>@C nanocomposite has a yolk–shell microsphere morphology with diameters of 1–2 μm, and both yolk and shell are composed of TiO<sub>2sub> nanoparticles (∼10 nm). The as-prepared yolk–shell TiO<sub>2sub>@C composites exhibit superior sodium storage properties, with a specific capacity of 210 mAh g<sup>–1sup>, an outstanding cycle life of 85% capacity retention of 2000 cycles and extraordinary rate performance at 40 C rate. All the results indicate that the yolk–shell TiO<sub>2sub>@C nanocomposite can be suggested as a promising anode material for high-performance sodium-ion batteries.