Photoactive/Passive Molecular Glass Blends: An Efficient Strategy to Optimize Azomaterials for Surface Relief Grating Inscription

详细信息    查看全文

• 作者：Audrey Laventure ; Jérémie Bourotte ; Jaana Vapaavuori ; Lucas Karperien ; Ribal Georges SabatOlivier Lebel ; Christian Pellerin
• 刊名：ACS Applied Materials & Interfaces
• 出版年：2017
• 出版时间：January 11, 2017
• 年：2017
• 卷：9
• 期：1
• 页码：798-808
• 全文大小：518K
• ISSN：1944-8252

文摘

Irradiation of azomaterials causes various photophysical and photomechanical effects that can be exploited for the preparation of functional materials such as surface relief gratings (SRGs). Herein, we develop and apply an efficient strategy to optimize the SRG inscription process by decoupling, for the first time, the important effects of the azo content and glass transition temperature (T_g). We prepare blends of a photoactive molecular glass functionalized with the azo Disperse Red 1 (gDR1) with a series of analogous photopassive molecular glasses. Blends with 10 and 40 mol % of gDR1 are completely miscible, present very similar optical properties, and cover a wide range of T_g from below to well above ambient temperature. SRG inscription experiments show that the diffraction efficiency (DE), residual DE, and initial inscription rate reach a maximum when T_g is 25–40 °C above ambient temperature for low to high azo content, respectively. Indeed, for a fixed 40 mol % azo content, choosing the optimal T_g enables doubling the SRG inscription rate and increasing DE 6-fold. Moreover, a higher azo content enables higher DE for a similar T_g. Spectroscopy measurements indicate that the photo-orientation of DR1 and its thermal stability are maximal with T_g around 70 °C, independent of the azo content. We conclude that the SRG potential of azomaterials depends on their capability to photo-orient but that the matrix rigidity eventually limits the inscription kinetics, leading to an optimal T_g that depends on the azo content. This study exposes clear material design guidelines to optimize the SRG inscription process and the photoactivity of azomaterials.