Asymmetric Pentagonal Metal Meshes for Flexible Transparent Electrodes and Heaters

详细信息    查看全文

• 作者：Daniel Lordan ; Micheal BurkeMary Manning ; Alfonso Martin ; Andreas Amann ; Dan O’Connell ; Richard Murphy ; Colin Lyons ; Aidan J. Quinn
• 刊名：ACS Applied Materials & Interfaces
• 出版年：2017
• 出版时间：February 8, 2017
• 年：2017
• 卷：9
• 期：5
• 页码：4932-4940
• 全文大小：504K
• ISSN：1944-8252

文摘

Metal meshes have emerged as an important class of flexible transparent electrodes. We report on the characteristics of a new class of asymmetric meshes, tiled using a recently discovered family of pentagons. Micron-scale meshes were fabricated on flexible polyethylene terephthalate substrates via optical lithography, metal evaporation (Ti 10 nm, Pt 50 nm), and lift-off. Three different designs were assessed, each with the same tessellation pattern and line width (5 μm), but with different sizes of the fundamental pentagonal unit. Good mechanical stability was observed for both tensile strain and compressive strain. After 1000 bending cycles, devices subjected to tensile strain showed fractional resistance increases in the range of 8–17%, while devices subjected to compressive strain showed fractional resistance increases in the range of 0–7%. The performance of the pentagonal metal mesh devices as visible transparent heaters via Joule heating was also assessed. Rapid response times (∼15 s) at low bias voltage (≤5 V) and good thermal resistance characteristics (213–258 °C cm²/W) were found using measured thermal imaging data. Deicing of an ice-bearing glass coupon on top of the transparent heater was also successfully demonstrated.