The dissolution of cubic and tetrahedral Pt nanoparticles has been studied on a Pt plate in 0.1 M NaClO4 using conventional in situ atomic force microscopy (AFM). The Pt nanoparticles were dissolved during the potential cycle between 0.0 and 1.1 V (Ag/AgCl). The sides of the nanoparticles are dissolved faster than the upper parts. The height of cubic Pt nanoparticles does not change up to 200 cycles, shrinking to 80% of the initial height after 600 cycles. Tetrahedral Pt nanoparticles are dissolved from the top, forming a terrace at the upper part after 300 cycles. The durability of cubic Pt nanoparticles is higher than that of tetrahedral Pt nanoparticles.