Impact of Nanostructure on Mechanical Properties of Norbornene-based Block Copolymers under Simulated Operating Conditions for Biobutanol Membranes

详细信息    查看全文

• 作者：Changhuai Ye ; Tamami Takigawa ; Oleksandr (Sasha) Burtovvy ; Leah Langsdorf ; Dane Jablonski ; Andrew Bell ; Bryan D. Vogt
• 刊名：ACS Applied Materials & Interfaces
• 出版年：2015
• 出版时间：June 10, 2015
• 年：2015
• 卷：7
• 期：22
• 页码：11765-11774
• 全文大小：455K
• ISSN：1944-8252

文摘

The structure and mechanical properties of a novel block copolymer (BCP) system with T_g鈥檚 for both segments exceeding 300 掳C, poly(butylnorbornene)-block-poly(hydroxyhexafluoroisopropyl norbornene) (BuNB-b-HFANB), are investigated as a function of processing conditions used for solvent vapor annealing (SVA). Solvent selection impacts long-range order markedly, but unexpectedly vertical orientation of cylinders are preferred over a wide range of solubility parameters, as determined by atomic force microscopy and grazing incidence small-angle X-ray scattering. The mechanical properties (elastic modulus, fracture strength, and onset fracture strain) are dependent upon the long-range order induced during SVA and determined using the combination of surface wrinkling and cracking. The modulus and fracture strength of the films increase from 1.44 GPa and 12.1 MPa to 1.77 GPa and 17.5 MPa, respectively, whereas the onset fracture strain decreases from 1.6% to approximately 0.6% as the ordering is improved. The polarity difference in the segments of the BCP is attractive for membrane separations, especially butanol鈥搘ater. For biobutanol recovery, the titers are typically <3 wt % butanol; exposure of the BCP membrane to aqueous 1 wt % butanol decreases the elastic modulus to approximately 0.90 GPa, irrespective of the morphology, despite the high T_g of both segments and limited swelling (5.0 wt %). Correspondingly, the onset fracture strain of these swollen films is estimated to increase significantly to 6鈥?%. These results indicate that operating conditions impact the mechanical performance of BCP membranes more than their morphology despite the high T_g of the neat copolymer. Wrinkling and cracking provide a facile route to test the mechanical properties of membranes under simulated operando conditions.