Inhibition by Poly(acrylic acid) and Morphological Changes in Calcium Carbonate and Calcium Carbonate/Calcium Sulfate Crystallization on Silica Fibers

详细信息    查看全文

• 作者：Ali A. Al-Hamzah ; Andrew D. Wallace ; Christopher P. East ; William O. S. Doherty ; Erica J. Smith ; Christopher M. Fellows
• 刊名：Industrial & Engineering Chemistry Research
• 出版年：2014
• 出版时间：May 28, 2014
• 年：2014
• 卷：53
• 期：21
• 页码：8793-8803
• 全文大小：601K
• 年卷期：v.53,no.21(May 28, 2014)
• ISSN：1520-5045

文摘

An intrinsic exposed core optical fiber sensor (IECOFS) made from fused silica was used to monitor the crystallization of calcium carbonate (CaCO₃) and CaCO₃/calcium sulfate (CaSO₄) composite at 100 and 120 掳C in the absence and presence of low-molar-mass (M_n 鈮?2000) poly(acrylic acid) (PAA) with different end groups. The IECOFS responded only to deposition and growth processes on the fiber surface rather than changes occurring in the bulk of the solution. Hexyl isobutyrate-terminated PAA (M_n = 1400) and hexadecyl isobutyrate-terminated PAA (M_n = 1700) were the most effective species in preventing CaCO₃ deposition. Phase transformation from vaterite to aragonite/calcite decreased with increasing hydrophobicity of the PAA end group. Low-molar-mass PAA at 10 ppm showed very significant inhibition of CaCO₃/CaSO₄ composite formation for all end groups investigated.