Glasses with nominal compositions SrFe10Al2O19+4(SrB2O4+Sr2B2O5) (1) and SrFe9Al3O19+4(SrB2O4+Sr2B2O5) (2) were prepared by rapid quenching of melts. Thermal treatment of glass samples at 600–900 °C resulted in crystallization of the magnetic phase SrFe12−xAlxO19 (x = 1.1±0.1) and strontium borates. Platelet hexaferrite particles with average sizes from (250×60) nm2 to (450×140) nm2 were prepared. The coercive force of glass ceramics is 580 and 475 kA m−1 for glasses 1 and 2, respectively. The coercive force of 580 kA m−1 is the highest known value compared to hexaferrite particles prepared earlier by glass crystallization.