刊名:Journal of Wuhan University of Technology-Mater. Sci. Ed.
出版年:2016
出版时间:December 2016
年:2016
卷:31
期:6
页码:1201-1205
全文大小:
刊物类别:Chemistry and Materials Science
刊物主题:Materials Science, general;
出版者:Wuhan University of Technology
ISSN:1993-0437
卷排序:31
文摘
Single-phase insulating 12CaO∙7Al2O3 (C12A7) powder was synthesized using an optimized hydrothermal method. Pure phase of C12A7 was got at a comparatively lower temperature (c.a. 300 °C) than that has been previously reported. The crystallite size of the synthesized C12A7 powder was 7±2 nm. The surface area values calculated for all the samples at a synthesis temperature range of 250-800 °C for 5 h were in the range of about 19-24 m2/g, with pore sizes of 12-20 nm. This low-temperature-based synthetic strategy along with nano porous structures and a high surface area value can facilitate catalyst application.